Anticorrosion behaviour of amorphous silicon-based coatings prepared by remote cold plasma-assisted chemical vapour deposition process
Article Sidebar
Main Article Content
Abstract
Organosilicon films were deposited on carbon steel samples using remote microwave nitrogen plasma-assisted chemical vapour deposition. The deposits were obtained using TetraMethyDisoloxane monomer mixed with oxygen. The formed films were characterised using electron microprobe analysis, Fourier transformed infrared spectroscopy, contact angle measurements, scanning electron microscopy and atomic force microscopy. The electrochemical properties of the organosilicon coatings were evaluated using gravimetric experiments next to electrochemical tests. A significant increase in the corrosion resistance behaviour of the organosilicon coated carbon steel specimen was found when the samples were immersed in 3% aqueous sodium chloride solutions. Also, the surface pre-treatment process of carbon steel had an important influence on the morphological and electrochemical behaviour. Argon pre-treatment improves significantly the corrosion resistance or organosilicon coated steel samples. Gravimetric tests in particular showed that samples pre-treated with argon result in lower weight loss and decreased corrosion rates compared to interfaces pre-treated with nitrogen plasma.
Keywords: PACVD, carbon steel, organ silicon, corrosion, pre-treatment, electrochemical impedance spectroscopy.
Downloads
Article Details
This work is licensed under a Creative Commons Attribution 4.0 International License.
Authors who publish with this journal agree to the following terms:- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).